Case of Crack Dynamics and Wallner Line in Fracture Analysis

Xiaolu Zhu

doi:10.16578/j.issn.1004.2539.2020.05.029

您当前的位置：

首页 >

文章列表页 >

Case of Crack Dynamics and Wallner Line in Fracture Analysis

Communication·Discussion | 更新时间：2022-11-10

- Case of Crack Dynamics and Wallner Line in Fracture Analysis
- Journal of Mechanical Transmission Vol. 44, Issue 5, Pages: 176-180(2020)
- 作者机构：
  
  1.北京科技大学,北京 100083
- 作者简介：
- 基金信息：
- DOI：10.16578/j.issn.1004.2539.2020.05.029
  CLC：
扫描看全文
朱孝录.断口分析中的裂纹动力学和瓦纳线实例[J].机械传动,2020,44(05):176-180.

Zhu Xiaolu.Case of Crack Dynamics and Wallner Line in Fracture Analysis[J].Journal of Mechanical Transmission,2020,44(05):176-180.
朱孝录.断口分析中的裂纹动力学和瓦纳线实例[J].机械传动,2020,44(05):176-180. DOI： 10.16578/j.issn.1004.2539.2020.05.029.

Zhu Xiaolu.Case of Crack Dynamics and Wallner Line in Fracture Analysis[J].Journal of Mechanical Transmission,2020,44(05):176-180. DOI： 10.16578/j.issn.1004.2539.2020.05.029.

摘要

在为材质42CrMo钢经锻造、调质和渗氮处理的曲轴断裂断口进行失效分析的案例中，发现断口上的贝纹线有相交的异常现象；这在一般的断口中是不可能出现的。用裂纹动力学和瓦纳线的理论对这种异常现象做了分析：由断口疲劳源处产生的裂纹，在扩展时会在材料中产生应力波，在裂纹所在的表面上传播。当裂纹遇到了不连续面，就会产生了一个横向的应力波，从而形成第二组以波源为圆心的同心圆弧，这才有可能出现贝纹线相交的现象。首次观察到瓦纳线不仅仅只能在金属与非金属脆性材料的断口上出现，文中以实例说明，在调质钢的断口上也可以出现瓦纳线。

Abstract

Abstract In the case of failure analysis of fracture of crankshaft with material 42CrMo, forged, tempered and nitriding treatment, it is found that there is an abnormal phenomenon of intersection of the scallop lines on the fracture surface. This is not possible in the general fracture surface. The crack dynamics and the theory of Wallner line are used to analyze the abnormal phenomenon, the crack at the source of fracture fatigue will produce stress wave in the material and propagate on the surface where the crack is located. When the crack encounters a discontinuous surface, a transverse stress wave is generated, thus forming a second set of concentric arcs centered at the wave source. This makes it possible for the shellfish lines to intersect. For the first time, it is observed that Wallner line cannot only appear on fracture surfaces of metallic and non-metallic brittle materials. It illustrates that Wallner line can also appear on the fracture surface of quenched and tempered steel.

关键词

断口分析裂纹动力学瓦纳线调质钢

Keywords

Fracture analysisCrack dynamicsWallner lineQuenched and tempered steel

references

钟群鹏，赵子华.断口学[M].北京：高等教育出版社，2006:314-169.

ZHONG Qunpeng,ZHAO Zihua.Fracture surface topography[M].Beijing:Higher Education Press,2006:314-169.

美国金属学会.金属手册:第10卷:失效分析与预防[M].周光垓,杨先琇,王仁智,等，译.8版.北京：机械工业出版社，1986：18.

American Society for Metals.Metals Handbook:Volume 10:Failure analysis and prevention[M].8th ed.ZHOU Guangai,YANG Xianxiou,WANG Renzhi,et al,Jr.Beijing:Machinery Industry Press，1986:18.

赫尔·D.断口形貌学——观察、测量和分析断口表面形貌的科学[M].李晓刚，董超芳，杜翠薇，译.北京：科学出版社，20099:262-273.

HULL Derek.Fractography——Observing,Measuring and Interpreting Fracture Surface Topography[M].LI Xiaogang,DONG Chaofang,DU Cuiwei,et al,Jr.Beijing:Science Press，2009:262-273.

于涛，谢红献，杜俊平，等.裂纹动力学的研究进展[J].金属功能材料，2008,15(3):39-42.

YU Tao,XIE Hongxian,DU Junping,et al.Development of Crack Dynamics[J].Metal Functional Materials,2008,15(3):39-42.

ROBERTO D,RICARDO J,PAUL V.Analytical model of dynamic crack evolution in tempered and strengthened glass plates[J].International Journal of Fracture,2014,190:75-86.

WALLNER H.Linienstrukturen an Bruchflachen[J].Z.Physik,1939(114):368-378.

亨利 G，豪斯特曼 D.宏观断口学及显微断口学[M].曾祥华，译.北京：机械工业出版社，1990：66.

HENRY G,HCRSTMANN D.Macro fracture and micro fracture［M］.ZENG Xianghua,Jr.Beijing:Machinery Industry Press，1990:66.

RABINOVITCH A,FRID V,BAHAT D.Wallner lines revisited[J].Journal of Applied Physics,2006,99(7):076102.

JIANG F C,KENNETH S V.Wallner lines in a nanocrystalline Ni–23% Fe alloy[J].Script Materialia，2012,67（11）:907-910.

ANDREWS EH.Stress waves and fracture surfaces[J].Journal of Applied Physics.1959,3(5):740-743.

崔约贤.金属断口分析[M].哈尔滨：哈尔滨工业大学出版社，1998:64-65.

CUI Yuexian.Fracture surface analysis of metals[M].Harbin:Harbin University of Technology Press,1998:64-65.

王璐，王志亮，石高扬，等.热处理花岗岩循环冲击下断口形貌研究[J].水利水运工程学报，2018(5):69-75.

WANG Lu,WANG Zhiliang,SHI Gaoyang,et al.Fracture morphology of heat treated granite under cyclic impact[J].Journal of Water Conservancy and Water Transport Engineering,2018(5):69-75.

WANG Meng,ZHAO Lü,MARION F,et al.Crack plane deflection and shear wave effects in the dynamic fracture of silicon single crystal[J].Journal of the Mechanics and Physics of Solids,2019(122):472-488.

ZORC B,NAGODE A.Determination of the crack-initiation and propagation conditions in a styrene-acrylonitrile water-filter housing with external ribs based on destructive pressure tests[J].Engineering Failure Analysis,2017(79):491-503.

ZAKAR F,BUDINSKI M.Fracture of a saddle fusion (weld) joint in high density polyethylene (HDPE) pipe[J].Engineering Failure Analysis,2017(82):481-492.

SCHNEIDER R.Quantitative fractography analysis of a chip crack in a Si power MOSFET[J].Microelectronics Reliability,2019,100/101:113361.

NARAYAN R L,TANDAIYA P,NARASIMBAN R,et al.Wallner lines,crack velocity and mechanisms of crack nucleation and growth in a brittle bulk metallic glass[J].Acta Materialia,2014,80:407-420.

布鲁克斯 C R，考霍莱 A.工程材料的失效分析[M].谢斐娟，孙家骧，译.北京：机械工业出版社，2003:202-203.

BROOKS C R,KOKHOLLEY A.Failure analysis of engineering materials[M].XIE Feijuan,SUN Jiaxiang,Jr.Beijing:Machinery Industry Press,2003:202-203.

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

No data

Related Author

No data

Related Institution

No data

⁰